Monolayer carbon dioxide barrier pet bottles

ABSTRACT

Disclosed herein are articles comprising polymer compositions that can provide a barrier to carbon dioxide diffusion. The disclosed polymer compositions can be utilized in packaging to retard or prevent the diffusion of carbon dioxide out of a carbonated liquid, inter alia, a carbonated soft drink. This abstract is intended as a scanning tool for purposes of searching in the particular art and is not intended to be limiting of the present invention.

CROSS REFERENCE TO RELATED APPLICATIONS

This application claims the benefit of priority to U.S. Utility application Ser. No. 13/612,064, filed Sep. 12, 2012, which claims the benefit of priority to U.S. Provisional Application No. 61/533,449, filed Sep. 12, 2011, which is hereby incorporated by reference in its entirety.

BACKGROUND

Carbon dioxide comprising beverages (carbonated beverages), inter alia, soda pop, beer, and the like, provide an organoleptic property that results in a “refreshing mouth-feel” when consumed. Carbonated beverages, especially carbonated soft drinks, must retain their carbonation in order to not be perceived as “flat.” Carbonated beverages that are packed in polyethylene terephthalate (PET) comprising containers can lose their amount of carbonation due to diffusion of carbon dioxide through the PET container.

Current solutions to solving the problem of CO₂ diffusion include providing a thicker container, however, this solution leads to an increased cost in the manufacturing of the container. Another solution is to provide a non-permeable barrier, for example, a resin. The added cost of the resin, as the modification of the equipment and processes for manufacturing PET contains makes this solution cost prohibitive. The addition of certain adjuncts, i.e., MXD6, would have an impact on the clarity and optical properties of the resulting PET polymer comprising container.

Therefore, there is a need for providing increased shelf life for carbonated beverages that does not involve increasing the thickness of the container walls, applying an expensive coating, admixing ingredients that impact container clarity, or any combination to these limitations.

SUMMARY

Disclosed herein are polymer compositions, comprising:

-   -   a) a base polymer;     -   b) from about 0.1% to about 10% by weight of a compound having         the formula:

-   -   -   wherein R¹ to R⁸ are each independently chosen from:         -   i) hydrogen;         -   ii) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclic alkyl;         -   iii) C₂-C₁₂ substituted or unsubstituted linear, branched,             or cyclic alkenyl;         -   iv) C₂-C₁₂ substituted or unsubstituted linear or branched             alkynyl;         -   v) C₆ or C₁₀ substituted or unsubstituted aryl;         -   vi) C₁-C₉ substituted or unsubstituted heterocyclic;         -   vii) C₁-C₁₁ substituted or unsubstituted heteroaryl;         -   viii) —[C(R^(10a))(R^(10b))]_(y)OR¹¹;             -   wherein R¹¹ is chosen from:             -   a) —H;             -   b) C₁-C₁₂ substituted or unsubstituted linear, branched,                 or cyclic alkyl or C₁-C₁₂ substituted or unsubstituted                 linear, branched, or cyclic haloalkyl;             -   c) C₆ or C₁₀ substituted or unsubstituted aryl or C₇-C₂₀                 alkylenearyl;             -   d) C₁-C₉ substituted or unsubstituted heterocyclic; and             -   e) C₁-C₁₁ substituted or unsubstituted heteroaryl;         -   ix) —[C(R^(10a))(R^(10b))]_(y)N(R^(12a))(R^(12b));             -   wherein R^(12a) and R^(12b) are each independently                 chosen from:             -   a) —H;             -   b) —OR¹³;                 -   R¹³ is hydrogen or C₁-C4 linear alkyl;             -   c) C₁-C₁₂ substituted or unsubstituted linear, branched,                 or cyclic alkyl;             -   d) C₆ or C₁₀ substituted or unsubstituted aryl;             -   e) C₁-C₉ substituted or unsubstituted heterocyclic;             -   f) C₁-C₁₁ substituted or unsubstituted heteroaryl; and             -   g) R^(12a) and R^(12b) can be taken together to form a                 substituted or unsubstituted ring having from 3 to 10                 carbon atoms and from 0 to 3 heteroatoms chosen from                 oxygen, nitrogen, and sulfur;         -   x) —[C(R^(10a))(R^(10b))]_(y)C(O)R¹⁴;             -   wherein R¹⁴ is chosen from:             -   a) C₁-C₁₂ substituted or unsubstituted linear, branched,                 or cyclic alkyl;             -   b) —OR¹⁵;                 -   wherein R¹⁵ is hydrogen, substituted or                     unsubstituted C₁-C₄ linear alkyl, C₆ or C₁₀                     substituted or unsubstituted aryl, C_(l)-C₉                     substituted or unsubstituted heterocyclic, C₁-C₁₁                     substituted or unsubstituted heteroaryl; and             -   c) —N(R^(16a))(R^(16b));                 -   wherein R^(16a) and R^(16b) are each independently                     hydrogen, C₁-C₁₂ substituted or unsubstituted                     linear, branched, or cyclic alkyl; C₆ or C₁₀                     substituted or unsubstituted aryl; C₁-C₉ substituted                     or unsubstituted heterocyclic; C₁-C₁₁ substituted or                     unsubstituted heteroaryl; or R^(16a) and R^(16b) can                     be taken together to form a substituted or                     unsubstituted ring having from 3 to 10 carbon atoms                     and from 0 to 3 heteroatoms chosen from oxygen,                     nitrogen, and sulfur;         -   xi) —[C(R^(10a))(R^(10b))]_(y)OC(O)R¹⁷;             -   wherein R¹⁷ is chosen from:             -   a) C₁-C₁₂ substituted or unsubstituted linear, branched,                 or cyclic alkyl; and             -   b) —N(R^(18a))(R^(18b));                 -   R^(18a) and R^(18b) are each independently hydrogen,                     C₁-C₁₂ substituted or unsubstituted linear,                     branched, or cyclic alkyl; C₆ or C₁₀ substituted or                     unsubstituted aryl; C₁-C₉ substituted or                     unsubstituted heterocyclic; C₁-C₁₁ substituted or                     unsubstituted heteroaryl; or R^(18a) and R^(18b) can                     be taken together to form a substituted or                     unsubstituted ring having from 3 to 10 carbon atoms                     and from 0 to 3 heteroatoms chosen from oxygen,                     nitrogen, and sulfur;         -   xii) —[C(R^(10a))(R^(10b))]_(y)NR¹⁹C(O)R²⁰;             -   wherein R¹⁸ is chosen from:             -   a) —H; and             -   b) C₁-C₄ substituted or unsubstituted linear, branched,                 or cyclic alkyl;             -   wherein R²⁰ is chosen from:             -   a) C₁-C₁₂ substituted or unsubstituted linear, branched,                 or cyclic alkyl; and             -   b) —N(R^(21a))(R^(21b));                 -   R^(21a) and R^(21b) are each independently hydrogen,                     C₁-C₁₂ substituted or unsubstituted linear,                     branched, or cyclic alkyl; C₆ or C₁₀ substituted or                     unsubstituted aryl; C₁-C₉ substituted or                     unsubstituted heterocyclic; C₁-C₁₁ substituted or                     unsubstituted heteroaryl; or R^(21a) and R^(21b) can                     be taken together to form a substituted or                     unsubstituted ring having from 3 to 10 carbon atoms                     and from 0 to 3 heteroatoms chosen from oxygen,                     nitrogen, and sulfur;         -   xiii) —[C(R^(10a))(R^(10b))]_(y)CN;         -   xiv) —[C(R^(10a))(R^(10b))]_(y)NO₂;         -   xv) —[C(R^(10a))(R^(10b))]_(y)SO₂R²²;             -   R²² is hydrogen, hydroxyl, substituted or unsubstituted                 C₁-C₄ linear or branched alkyl; substituted or                 unsubstituted C₆, C₁₀, or C₁₄ aryl; C₇-C₁₅ alkylenearyl;                 C₁-C₉ substituted or unsubstituted heterocyclic; or                 C₁-C₁₁ substituted or unsubstituted heteroaryl; and         -   xvi) halogen;         -   xvii)             —[C(R^(10a))(R^(10b))]_(y)(CH_(j′)X_(k′))_(h)CH_(j)X_(k);             wherein X is halogen, the index j is an integer from 0 to 2,             the index k is an integer from 1 to 3, j+k=3; the index j′             is an integer from 0 to 2, the index k′ is and integer from             0 to 2, j′+k′=2; the index h is from 0 to 5;         -   R^(10a) and R^(10b) are each independently hydrogen or C₁-C₄             alkyl; and         -   the index y is from 0 to 5;

R¹ and R⁸ can be taken together to from a 5 to 7 member ring containing from 3 to 7 carbon atoms and from 0 to 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms can be substituted, unsubstituted, or a carbonyl unit.

Also disclosed herein are methods of making the compositions, articles comprising the compositions, and methods of making the articles.

Additional advantages of the invention will be set forth in part in the description which follows, and in part will be obvious from the description, or can be learned by practice of the invention. The advantages of the invention will be realized and attained by means of the elements and combinations particularly pointed out in the appended claims. It is to be understood that both the foregoing general description and the following detailed description are exemplary and explanatory only and are not restrictive of the invention, as claimed.

BRIEF DESCRIPTION OF THE FIGURES

The accompanying figures, which are incorporated in and constitute a part of this specification, illustrate several aspects and together with the description serve to explain the principles of the invention.

FIG. 1 shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 1.

FIG. 2(a) shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 1.

FIG. 2(b) shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 1.

FIG. 3(a) shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 1.

FIG. 3(b) shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 1.

FIG. 4 shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 2.

FIG. 5 shows representative CO₂ loss data for the disclosed polymer compositions as described below in Example 2.

DETAILED DESCRIPTION

The present invention can be understood more readily by reference to the following detailed description of the invention and the Examples included therein.

Before the present compounds, compositions, articles, systems, devices, and/or methods are disclosed and described, it is to be understood that they are not limited to specific synthetic methods unless otherwise specified, or to particular reagents unless otherwise specified, as such can, of course, vary. It is also to be understood that the terminology used herein is for the purpose of describing particular aspects only and is not intended to be limiting. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, example methods and materials are now described.

Unless defined otherwise, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. Although any methods and materials similar or equivalent to those described herein can be used in the practice or testing of the present invention, example methods and materials are now described.

In this specification and in the claims that follow, reference will be made to a number of terms, which shall be defined to have the following meanings:

All percentages, ratios and proportions herein are by weight, unless otherwise specified. All temperatures are in degrees Celsius (° C.) unless otherwise specified.

Throughout the description and claims of this specification the word “comprise” and other forms of the word, such as “comprising” and “comprises,” means including but not limited to, and is not intended to exclude, for example, other additives, components, integers, or steps.

As used in the description and the appended claims, the singular forms “a,” “an,” and “the” include plural referents unless the context clearly dictates otherwise. Thus, for example, reference to “a composition” includes mixtures of two or more such compositions, reference to “a phenylsulfamic acid” includes mixtures of two or more such phenylsulfamic acids, reference to “the compound” includes mixtures of two or more such compounds, and the like.

“Optional” or “optionally” means that the subsequently described event or circumstance can or cannot occur, and that the description includes instances where the event or circumstance occurs and instances where it does not.

Ranges can be expressed herein as from “about” one particular value, and/or to “about” another particular value. When such a range is expressed, another aspect includes from the one particular value and/or to the other particular value. Similarly, when values are expressed as approximations, by use of the antecedent “about,” it will be understood that the particular value forms another aspect. It will be further understood that the endpoints of each of the ranges are significant both in relation to the other endpoint, and independently of the other endpoint. It is also understood that there are a number of values disclosed herein, and that each value is also herein disclosed as “about” that particular value in addition to the value itself. For example, if the value “10” is disclosed, then “about 10” is also disclosed. It is also understood that when a value is disclosed, then “less than or equal to” the value, “greater than or equal to the value,” and possible ranges between values are also disclosed, as appropriately understood by the skilled artisan. For example, if the value “10” is disclosed, then “less than or equal to 10” as well as “greater than or equal to 10” is also disclosed. It is also understood that throughout the application data are provided in a number of different formats and that this data represent endpoints and starting points and ranges for any combination of the data points. For example, if a particular data point “10” and a particular data point “15” are disclosed, it is understood that greater than, greater than or equal to, less than, less than or equal to, and equal to 10 and 15 are considered disclosed as well as between 10 and 15. It is also understood that each unit between two particular units are also disclosed. For example, if 10 and 15 are disclosed, then 11, 12, 13, and 14 are also disclosed.

As used herein, the term “substantially” means that the subsequently described event or circumstance completely occurs or that the subsequently described event or circumstance generally, typically, or approximately occurs. For example, when the specification discloses that substantially all of an agent is released, a person skilled in the relevant art would readily understand that the agent need not be completely released. Rather, this term conveys to a person skilled in the relevant art that the agent need only be released to an extent that an effective amount is no longer unreleased.

As used herein, the term “polymer” refers to a relatively high molecular weight organic compound, natural or synthetic, whose structure can be represented by a repeated small unit, the monomer (e.g., polyethylene, rubber, cellulose). Synthetic polymers are typically formed by addition or condensation polymerization of monomers.

As used herein, the term “copolymer” refers to a polymer formed from two or more different repeating units (monomer residues). By way of example and without limitation, a copolymer can be an alternating copolymer, a random copolymer, a block copolymer, or a graft copolymer. It is also contemplated that, in certain aspects, various block segments of a block copolymer can themselves comprise copolymers.

As used herein, the term “oligomer” refers to a relatively low molecular weight polymer in which the number of repeating units is between two and ten, for example, from two to eight, from two to six, or form two to four. In one aspect, a collection of oligomers can have an average number of repeating units of from about two to about ten, for example, from about two to about eight, from about two to about six, or form about two to about four.

As used herein, the term “star polymer” refers to a branched polymer molecule in which a single branch point gives rise to multiple linear chains or arms. The single branch point can be a single chemical moiety or can be a highly crosslinked section of polymer. In one aspect, a star polymer can be generally spherical in shape. In a further aspect, a star polymer can be particle shaped. If the arms are identical the star polymer molecule is said to be regular. If adjacent arms are composed of different repeating subunits, the star polymer molecule is said to be variegated.

As used herein, the term “molecular weight” (MW) refers to the mass of one molecule of that substance, relative to the unified atomic mass unit u (equal to 1/12 the mass of one atom of carbon-12).

As used herein, the term “number average molecular weight” (M_(n)) refers to the common, mean, average of the molecular weights of the individual polymers. M_(n) can be determined by measuring the molecular weight of n polymer molecules, summing the weights, and dividing by n. M_(n) is calculated by:

${{\overset{\_}{M}}_{n} = \frac{\sum_{i}{N_{i}M_{i}}}{\sum_{i}N_{i}}},$

wherein N_(i) is the number of molecules of molecular weight M_(i). The number average molecular weight of a polymer can be determined by gel permeation chromatography, viscometry (Mark-Houwink equation), light scattering, analytical ultracentrifugation, vapor pressure osmometry, end-group titration, and colligative properties.

As used herein, the term “weight average molecular weight” (M_(w)) refers to an alternative measure of the molecular weight of a polymer. M_(w) is calculated by:

${{\overset{\_}{M}}_{w} = \frac{\sum_{i}{N_{i}M_{i}^{2}}}{\sum_{i}{N_{i}M_{i}}}},$

wherein N_(i) is the number of molecules of molecular weight M_(i). Intuitively, if the weight average molecular weight is w, and a random monomer is selected, then the polymer it belongs to will have a weight of w on average. The weight average molecular weight can be determined by light scattering, small angle neutron scattering (SANS), X-ray scattering, and sedimentation velocity.

As used herein, the terms “polydispersity” and “polydispersity index” (PDI) refer to the ratio of the weight average to the number average (M_(w)/M_(n)).

As used herein, the term “compatibilizing agent” refers to a small molecule or polymer that has both polar and non-polar functional groups. For example, a fatty-acid ester has both polar and non-polar functional groups.

A weight percent (wt. %) of a component, unless specifically stated to the contrary, is based on the total weight of the formulation or composition in which the component is included.

As used herein, nomenclature for compounds, including organic compounds, can be given using common names, IUPAC, IUBMB, or CAS recommendations for nomenclature. When one or more stereochemical features are present, Cahn-Ingold-Prelog rules for stereochemistry can be employed to designate stereochemical priority, E/Z specification, and the like. One of skill in the art can readily ascertain the structure of a compound if given a name, either by systemic reduction of the compound structure using naming conventions, or by commercially available software, such as CHEMDRAW™ (Cambridgesoft Corporation, U.S.A.).

The following chemical hierarchy is used throughout the specification to describe and enable the scope of the present disclosure and to particularly point out and distinctly claim the units which comprise the compounds of the present disclosure, however, unless otherwise specifically defined, the terms used herein are the same as those of the artisan of ordinary skill. The term “hydrocarbyl” stands for any carbon atom-based unit (organic molecule), said units optionally containing one or more organic functional group, including inorganic atom comprising salts, inter alia, carboxylate salts, quaternary ammonium salts. Within the broad meaning of the term “hydrocarbyl” are the classes “acyclic hydrocarbyl” and “cyclic hydrocarbyl” which terms are used to divide hydrocarbyl units into cyclic and non-cyclic classes.

As it relates to the following definitions, “cyclic hydrocarbyl” units can comprise only carbon atoms in the ring (i.e., carbocyclic and aryl rings) or can comprise one or more heteroatoms in the ring (i.e., heterocyclic and heteroaryl rings). For “carbocyclic” rings the lowest number of carbon atoms in a ring are 3 carbon atoms; cyclopropyl. For “aryl” rings the lowest number of carbon atoms in a ring are 6 carbon atoms; phenyl. For “heterocyclic” rings the lowest number of carbon atoms in a ring is 1 carbon atom; diazirinyl. Ethylene oxide comprises 2 carbon atoms and is a C₂ heterocycle. For “heteroaryl” rings the lowest number of carbon atoms in a ring is 1 carbon atom; 1,2,3,4-tetrazolyl. The following is a non-limiting description of the terms “acyclic hydrocarbyl” and “cyclic hydrocarbyl” as used herein.

-   A. Substituted and unsubstituted acyclic hydrocarbyl:     -   For the purposes of the present disclosure the term “substituted         and unsubstituted acyclic hydrocarbyl” encompasses 3 categories         of units: -   1) linear or branched alkyl, non-limiting examples of which include,     methyl (C₁), ethyl (C₂), n-propyl (C₃), iso-propyl (C₃), n-butyl     (C₄), sec-butyl (C₄), iso-butyl (C₄), tert-butyl (C₄), and the like;     substituted linear or branched alkyl, non-limiting examples of which     includes, hydroxymethyl (C₁), chloromethyl (C₁), trifluoromethyl     (C₁), aminomethyl (C₁), 1-chloroethyl (C₂), 2-hydroxyethyl (C₂),     1,2-difluoroethyl (C₂), 3-carboxypropyl (C₃), and the like. -   2) linear or branched alkenyl, non-limiting examples of which     include, ethenyl (C₂), 3-propenyl (C₃), 1-propenyl (also     2-methylethenyl) (C₃), isopropenyl (also 2-methylethen-2-yl) (C₃),     buten-4-yl (C₄), and the like; substituted linear or branched     alkenyl, non-limiting examples of which include, 2-chloroethenyl     (also 2-chlorovinyl) (C₂), 4-hydroxybuten-1-yl (C₄),     7-hydroxy-7-methyloct-4-en-2-yl (C₉),     7-hydroxy-7-methyloct-3,5-dien-2-yl (C₉), and the like. -   3) linear or branched alkynyl, non-limiting examples of which     include, ethynyl (C₂), prop-2-ynyl (also propargyl) (C₃),     propyn-1-yl (C₃), and 2-methyl-hex-4-yn-1-yl (C₇); substituted     linear or branched alkynyl, non-limiting examples of which include,     5-hydroxy-5-methylhex-3-ynyl (C₇), 6-hydroxy-6-methylhept-3-yn-2-yl     (C₈), 5-hydroxy-5-ethylhept-3-ynyl (C₉), and the like. -   B. Substituted and unsubstituted cyclic hydrocarbyl:     -   For the purposes of the present disclosure the term “substituted         and unsubstituted cyclic hydrocarbyl” encompasses 5 categories         of units: -   1) The term “carbocyclic” is defined herein as “encompassing rings     comprising from 3 to 20 carbon atoms, wherein the atoms which     comprise said rings are limited to carbon atoms, and further each     ring can be independently substituted with one or more moieties     capable of replacing one or more hydrogen atoms.” The following are     non-limiting examples of “substituted and unsubstituted carbocyclic     rings” which encompass the following categories of units:     -   i) carbocyclic rings having a single substituted or         unsubstituted hydrocarbon ring, non-limiting examples of which         include, cyclopropyl (C₃), 2-methyl-cyclopropyl (C₃),         cyclopropenyl (C₃), cyclobutyl (C₄), 2,3-dihydroxycyclobutyl         (C₄), cyclobutenyl (C₄), cyclopentyl (C₅), cyclopentenyl (C₅),         cyclopentadienyl (C₅), cyclohexyl (C₆), cyclohexenyl (C₆),         cycloheptyl (C₇), cyclooctanyl (C₈), 2,5-dimethylcyclopentyl         (C₅), 3,5-dichlorocyclohexyl (C₆), 4-hydroxycyclohexyl (C₆), and         3,3,5-trimethylcyclohex-1-yl (C₆).     -   ii) carbocyclic rings having two or more substituted or         unsubstituted fused hydrocarbon rings, non-limiting examples of         which include, octahydropentalenyl (C₈), octahydro-1H-indenyl         (C₉), 3a,4,5,6,7,7a-hexahydro-3H-inden-4-yl (C₉),         decahydroazulenyl (C₁₀).     -   iii) carbocyclic rings which are substituted or unsubstituted         bicyclic hydrocarbon rings, non-limiting examples of which         include, bicyclo-[2.1.1]hexanyl, bicyclo[2.2.1]heptanyl,         bicyclo[3.1.1]heptanyl, 1,3-dimethyl[2.2.1]heptan-2-yl,         bicyclo[2.2.2]octanyl, and bicyclo[3.3.3]undecanyl. -   2) The term “aryl” is defined herein as “units encompassing at least     one phenyl or naphthyl ring and wherein there are no heteroaryl or     heterocyclic rings fused to the phenyl or naphthyl ring and further     each ring can be independently substituted with one or more moieties     capable of replacing one or more hydrogen atoms.” The following are     non-limiting examples of “substituted and unsubstituted aryl rings”     which encompass the following categories of units:     -   i) C₆ or C₁₀ substituted or unsubstituted aryl rings; phenyl and         naphthyl rings whether substituted or unsubstituted,         non-limiting examples of which include, phenyl (C₆),         naphthylen-1-yl (C₁₀), naphthylen-2-yl (C₁₀), 4-fluorophenyl         (C₆), 2-hydroxyphenyl (C₆), 3-methylphenyl (C₆),         2-amino-4-fluorophenyl (C₆), 2-(N,N-diethylamino)phenyl (C₆),         2-cyanophenyl (C₆), 2,6-di-tert-butylphenyl (C₆),         3-methoxyphenyl (C₆), 8-hydroxynaphthylen-2-yl (C₁₀),         4,5-dimethoxynaphthylen-1-yl (C₁₀) and 6-cyano-naphthylen-1-yl         (C₁₀).     -   ii) C₆ or C₁₀ aryl rings fused with 1 or 2 saturated rings to         afford C₈-C₂₀ ring systems, non-limiting examples of which         include, bicyclo[4.2.0]octa-1,3,5-trienyl (C₈), and indanyl         (C₉). -   3) The terms “heterocyclic” and/or “heterocycle” are defined herein     as “units comprising one or more rings having from 3 to 20 atoms     wherein at least one atom in at least one ring is a heteroatom     chosen from nitrogen (N), oxygen (O), or sulfur (S), or mixtures of     N, O, and S, and wherein further the ring which contains the     heteroatom is also not an aromatic ring.” The following are     non-limiting examples of “substituted and unsubstituted heterocyclic     rings” which encompass the following categories of units:     -   -   i) heterocyclic units having a single ring containing one or             more heteroatoms, non-limiting examples of which include,             diazirinyl (C₁), aziridinyl (C₂), urazolyl (C₂), azetidinyl             (C₃), pyrazolidinyl (C₃), imidazolidinyl (C₃), oxazolidinyl             (C₃), isoxazolinyl (C₃), thiazolidinyl (C₃), isothiazolinyl             (C₃), oxathiazolidinonyl (C₃), oxazolidinonyl (C₃),             hydantoinyl (C₃), tetrahydrofuranyl (C₄), pyrrolidinyl (C₄),             morpholinyl (C₄), piperazinyl (C₄), piperidinyl (C₄),             dihydropyranyl (C₅), tetrahydropyranyl (C₅),             piperidin-2-onyl (valerolactam) (C₅),             2,3,4,5-tetrahydro-1H-azepinyl (C₆), 2,3-dihydro-1H-indole             (C₈), and 1,2,3,4-tetrahydroquinoline (C₉).         -   ii) heterocyclic units having 2 or more rings one of which             is a heterocyclic ring, non-limiting examples of which             include hexahydro-1H-pyrrolizinyl (C₇),             3a,4,5,6,7,7a-hexahydro-1H-benzo[d]imidazolyl (C₇),             3a,4,5,6,7,7a-hexahydro-1H-indolyl (C₈),             1,2,3,4-tetrahydroquinolinyl (C₉), and             decahydro-1H-cycloocta[b]pyrrolyl (C₁₀). -   4) The term “heteroaryl” is defined herein as “encompassing one or     more rings comprising from 5 to 20 atoms wherein at least one atom     in at least one ring is a heteroatom chosen from nitrogen (N),     oxygen (O), or sulfur (S), or mixtures of N, O, and S, and wherein     further at least one of the rings which comprises a heteroatom is an     aromatic ring.” The following are non-limiting examples of     “substituted and unsubstituted heterocyclic rings” which encompass     the following categories of units:     -   i) heteroaryl rings containing a single ring, non-limiting         examples of which include, 1,2,3,4-tetrazolyl (C₁),         [1,2,3]triazolyl (C₂), [1,2,4]triazolyl (C₂), triazinyl (C₃),         thiazolyl (C₃), 1H-imidazolyl (C₃), oxazolyl (C₃), isoxazolyl         (C₃), isothiazolyl (C₃), furanyl (C₄), thiophenyl (C₄),         pyrimidinyl (C₄), 2-phenylpyrimidinyl (C₄), pyridinyl (C₅),         3-methylpyridinyl (C₅), and 4-dimethylaminopyridinyl (C₅)     -   ii) heteroaryl rings containing 2 or more fused rings one of         which is a heteroaryl ring, non-limiting examples of which         include: 7H-purinyl (C₅), 9H-purinyl (C₅), 6-amino-9H-purinyl         (C₅), 5H-pyrrolo[3,2-d]pyrimidinyl (C₆),         7H-pyrrolo[2,3-d]pyrimidinyl (C₆), pyrido[2,3-d]pyrimidinyl         (C₇), 2-phenylbenzo[d]thiazolyl (C₇), 1H-indolyl (C₈),         4,5,6,7-tetrahydro-1-H-indolyl (C₈), quinoxalinyl (C₈),         5-methylquinoxalinyl (C₈), quinazolinyl (C₈), quinolinyl (C₉),         8-hydroxy-quinolinyl (C₉), and isoquinolinyl (C₉). -   5) C_(l)-C₆ tethered cyclic hydrocarbyl units (whether carbocyclic     units, C₆ or C₁₀ aryl units, heterocyclic units, or heteroaryl     units) which connected to another moiety, unit, or core of the     molecule by way of a C₁-C₆ alkylene unit. Non-limiting examples of     tethered cyclic hydrocarbyl units include benzyl C₁-(C₆) having the     formula:

-   -   wherein R^(a) is optionally one or more independently chosen         substitutions for hydrogen. Further examples include other aryl         units, inter alia, (2-hydroxyphenyl)hexyl C₆-(C₆);         naphthalen-2-ylmethyl C₁-(C₁₀), 4-fluorobenzyl C₁-(C₆),         2-(3-hydroxyphenyl)ethyl C₂-(C₆), as well as substituted and         unsubstituted C₃-C₁₀ alkylenecarbocyclic units, for example,         cyclopropylmethyl C₁-(C₃), cyclopentylethyl C₂-(C₅),         cyclohexylmethyl C₁-(C₆);. Included within this category are         substituted and unsubstituted C₁-C₁₀ alkylene-heteroaryl units,         for example a 2-picolyl C₁-(C₆) unit having the formula:

-   -   wherein R^(a) is the same as defined above. In addition, C₁-C₁₂         tethered cyclic hydrocarbyl units include C₁-C₁₀         alkyleneheterocyclic units and alkylene-heteroaryl units,         non-limiting examples of which include, aziridinylmethyl C₁-(C₂)         and oxazol-2-ylmethyl C₁-(C₃).

For the purposes of the present disclosure carbocyclic rings are from C₃ to C₂₀; aryl rings are C₆ or C₁₀; heterocyclic rings are from C₁ to C₉; and heteroaryl rings are from C₁ to C₉.

For the purposes of the present disclosure, and to provide consistency in defining the present disclosure, fused ring units, as well as spirocyclic rings, bicyclic rings and the like, which comprise a single heteroatom will be characterized and referred to herein as being encompassed by the cyclic family corresponding to the heteroatom containing ring, although the artisan may have alternative characterizations. For example, 1,2,3,4-tetrahydroquinoline having the formula:

is, for the purposes of the present disclosure, considered a heterocyclic unit. 6,7-Dihydro-5H-cyclopentapyrimidine having the formula:

is, for the purposes of the present disclosure, considered a heteroaryl unit. When a fused ring unit contains heteroatoms in both a saturated ring (heterocyclic ring) and an aryl ring (heteroaryl ring), the aryl ring will predominate and determine the type of category to which the ring is assigned herein for the purposes of describing the invention. For example, 1,2,3,4-tetrahydro-[1,8]naphthpyridine having the formula:

is, for the purposes of the present disclosure, considered a heteroaryl unit.

The term “substituted” is used throughout the specification. The term “substituted” is applied to the units described herein as “substituted unit or moiety is a hydrocarbyl unit or moiety, whether acyclic or cyclic, which has one or more hydrogen atoms replaced by a substituent or several substituents as defined herein below.” The units, when substituting for hydrogen atoms are capable of replacing one hydrogen atom, two hydrogen atoms, or three hydrogen atoms of a hydrocarbyl moiety at a time. In addition, these substituents can replace two hydrogen atoms on two adjacent carbons to form said substituent, new moiety, or unit. For example, a substituted unit that requires a single hydrogen atom replacement includes halogen, hydroxyl, and the like. A two hydrogen atom replacement includes carbonyl, oximino, and the like. A two hydrogen atom replacement from adjacent carbon atoms includes epoxy, and the like. Three hydrogen replacement includes cyano, and the like. The term substituted is used throughout the present specification to indicate that a hydrocarbyl moiety, inter alfa, aromatic ring, alkyl chain; can have one or more of the hydrogen atoms replaced by a substituent. When a moiety is described as “substituted” any number of the hydrogen atoms may be replaced. For example, 4-hydroxyphenyl is a “substituted aromatic carbocyclic ring (aryl ring)”, (N,N-dimethyl-5-amino)octanyl is a “ substituted C₈ linear alkyl unit, 3-guanidinopropyl is a “substituted C₃ linear alkyl unit,” and 2-carboxypyridinyl is a “substituted heteroaryl unit.”

Polymer Compositions

Disclosed herein are polymer compositions, comprising

-   -   a) a base polymer;     -   b) from about 0.1% to about 10% by weight of an oxygen         scavenger; and     -   c) from about 0.1% to about 10% by weight of a compound further         described herein below.

Base Polymers

The disclosed compositions comprise a base polymer. The base polymer can comprise one or more homopolymers or copolymers as described herein. The compositions can comprise from about 80% to about 99.98% by weight of a base polymer. In one embodiment the composition comprises from about 80% to about 99% by weight of a base polymer. In another embodiment the composition comprises from about 85% to about 99% by weight of a base polymer. In a further embodiment the composition comprises from about 90% to about 99.98% by weight of a base polymer. In a yet further embodiment the composition comprises from about 95% to about 99% by weight of a base polymer. In a still further embodiment the composition comprises from about 95% to about 99.98% by weight of a base polymer. In a yet another embodiment the composition comprises from about 97% to about 99% by weight of a base polymer.

A variety of different polymers can be used as the base polymer. The disclosed compositions enable oxygen scavenging, and thus the base polymer generally includes those polymers that can be subject to oxidation. For example, polymers that exhibit at least some oxygen permeability are useful with the disclosed compositions, at least inasmuch as the disclosed compositions can reduce the oxidative damage to the polymer.

The base polymer can be a polymer commonly used in packaging materials including polyethylene, such as low density polyethylene, very low density polyethylene, ultra-low density polyethylene, high density polyethylene, and linear low density polyethylene; polyesters such as (PET), (PEN) and their copolymers such as PET/IP; polyvinyl chloride (PVC); polyvinylidene chloride (PVDC); and ethylene copolymers such as ethylene/vinyl acetate copolymer, ethylene/alkyl (meth)acrylate copolymers, ethylene/(meth)acrylic acid copolymers, and ionomers. Blends of different base polymers also can be used.

In a further aspect, the base polymer can include one or more polymers approved by the U.S. Food and Drug Administration (FDA). Examples include polyethylene terephthalate, polypropylene, and polyethylene.

In a further aspect, the base polymer comprises a polyester polymer or copolymer. Preferred polyesters include polymers of phthalic acids, such as polyethylene terephthalate (PET), or a copolymer thereof. PET, for example, can be made from terephthalic acid and ethylene glycol. PET can also be made using dimethyl terephthalate and ethylene glycol. Preferred copolymers of phthalic acids include copolymers of a phthalic acid and one or more hydroxylated organic compounds. Examples of suitable hydroxylated organic compounds include 1,4-cyclohexandedimethanol, 1,2-propanediol, 1,4-butanediol, 2,2-dimethyl-1,3-propanediol, 2-methyl -1,3 -propanediol (2MPDO), 1,6-hexanediol, 1,2-cyclohexanediol, 1,4-cyclohexanediol, 1,2-cyclohexanedimethanol, 1,3-cyclohexanedimethanol, and diols containing one or more oxygen atoms in the chain, e.g., diethylene glycol, triethylene glycol, dipropylene glycol, tripropylene glycol, or mixtures of these, and the like.

In a still further aspect, the base polymer includes a polyethylene terephthalate homopolymer and copolymer modified with one or more polycarboxylic acid modifiers in a cumulative amount of less than about 15 mole %, or about 10 mole % or less, or about 8 mole % or less, or one or more hydroxyl compound modifiers in an amount of less than about 60 mol %, or less than about 50 mole %, or less than about 40 mole %, or less than about 15 mole %, or about 10 mole % or less, or about 8 mole % or less and polyethylene naphthalate homopolymers and copolymers modified with a cumulative amount of less than about 15 mole %, or about 10 mole % or less, or about 8 mole % or less, of one or more polycarboxylic acid modifiers or modified with less than about 60 mol %, or less than about 50 mole %, or less than about 40 mole %, or less than about 15 mole %, or about 10 mole % or less, or about 8 mole % or less of one or more hydroxyl compound modifiers, and blends thereof. In some aspects, the base polymer comprises at least 90 mole %, 92 mole %, or 94 mole % ethylene terephthalate repeat units based on the moles of all repeat units in the polyester polymers.

Polyesters such as PET can be prepared by polymerization procedures known in the art sufficient to effect esterification and polycondensation. Polyester melt phase manufacturing processes include direct condensation of a dicarboxylic acid with a diol, optionally in the presence of one or more esterification catalysts, in the esterification zone, followed by polycondensation in the prepolymer and finishing zones in the presence of a polycondensation catalyst; or ester exchange usually in the presence of a transesterification catalyst in the ester exchange zone, followed by prepolymerization and polymerization in the presence of a polycondensation catalyst.

Oxygen Scavenger

The compositions comprise from about 0.10% to about 10% weight percent of the oxygen scavenger. In one embodiment the compositions comprise from about 0.5% to about 10% by weight of an oxygen scavenger. In another embodiment the compositions comprise from about 1% to about 5% by weight of an oxygen scavenger. In a further embodiment the compositions comprise from about 0.1% to about 1% by weight of an oxygen scavenger. In a still further embodiment the compositions comprise from about 0.1% to about 5% by weight of an oxygen scavenger. In a yet further embodiment the compositions comprise from about 3% to about 10% by weight of an oxygen scavenger. In another further embodiment the compositions comprise from about 5% to about 10% by weight of an oxygen scavenger. In a yet another embodiment the compositions comprise from about 2% to about 7% by weight of an oxygen scavenger.

Preferably, the oxygen scavenger is an N-allylic oxygen scavenger or N-benzylic oxygen scavenger. The oxygen scavenger can function as an oxygen scavenger in the composition. The oxygen scavenging ability of the oxygen scavenger can be enhanced by the transition metal.

N-allylic or N-benzylic oxygen scavengers have the general structure shown below:

wherein each

independently denotes an optional covalent bond.

-   It is also appreciated that an N-allylic or N-benzylic oxygen     scavenger can be further substituted and that more than one amide     functionality can be present in a compound. In one aspect, an     N-allylic or N-benzylic oxygen scavenger can be polymeric. In a     further aspect, an N-allylic or N-benzylic oxygen scavenger can be     nonpolymeric.

Generally, the oxygen scavenger is present in the composition in an amount of from 0.1 to about 10 weight percent. In one aspect, the oxygen scavenger is present in the composition in an amount of from 1 to about 10 weight percent. In a further aspect, the oxygen scavenger is present in the composition in an amount of from 1 to about 5 weight percent. In a further aspect, the oxygen scavenger is present in the composition in an amount of from 1 to about 3 weight percent.

In one aspect, the oxygen scavenger has a structure of Formula I:

wherein each X is selected from the group consisting of O, S, and NH; wherein each Y, each A, and each B are independently selected from the group consisting of N and CR¹; wherein D, E, and F are independently selected from the group consisting of CH, N, O, and S; wherein the symbol

when used in conjunction with a bond line represents a single or a double bond; and wherein each R¹ is independently selected from the group consisting of H, alkyl, aryl, electron withdrawing groups, and electron releasing groups.

In a further aspect, the oxygen scavenger has a structure of Formula II:

wherein each X is selected from the group consisting of O, S, and NH; wherein each Y, each A, and each B are independently selected from the group consisting of N and CR²; wherein D, E, and F are independently selected from the group consisting of CH, N, O, and S; wherein the symbol

when used in conjunction with a bond line represents a single or a double bond; and wherein each R² is independently selected from the group consisting of H, alkyl, aryl, electron withdrawing groups, and electron releasing groups.

The alkyl group of Formula (I) or (II) can be a branched or unbranched saturated hydrocarbon group of 1 to 24 carbon atoms, e.g. 1 to 18 carbons atoms, 1 to 14 carbon atoms, 1 to 12 carbon atoms, 1 to 10 carbon atoms, 1 to 8, 1 to 6 carbon atoms, or 1 to 4 carbon atoms, such as methyl, ethyl, n-propyl, isopropyl, n-butyl, isobutyl, t-butyl, pentyl, hexyl, heptyl, octyl, decyl, tetradecyl, hexadecyl, eicosyl, tetracosyl and the like. The alkyl group can be substituted or unsubstituted. The alkyl group can be substituted with one or more groups including, but not limited to, alkyl, halogenated alkyl, alkoxy, alkenyl, alkynyl, aryl, heteroaryl, aldehyde, amino, carboxylic acid, ester, halide, hydroxamate, hydroxy, ketone, nitro, silyl, sulfo-oxo, sulfonyl, sulfone, sulfoxide, or thiol, as described below. The alkyl group can be halogenated, which includes an alkyl group that is substituted with one or more halide, e.g., fluorine, chlorine, bromine, or iodine. The alkyl group can also be a lower alkyl group, which is an alkyl group containing from one to six (e.g., from one to four) carbon atoms.

The aryl group of Formula (I) or (II) can be any carbon-based aromatic group including but not limited to, benzene, naphthalene, phenyl, biphenyl, etc. The aryl group can also be heteroaryl, which is defined as an aromatic group that has at least one heteroatom incorporated within the ring of the aromatic group. Examples of heteroatoms include, but are not limited to, nitrogen, oxygen, sulfur, and phosphorus. The aryl group can be substituted or unsubstituted. The aryl group can be substituted with one or more groups including, but not limited to, alkyl, halogenated alkyl, alkoxy, alkenyl, alkynyl, aryl, heteroaryl, aldehyde, amino, carboxylic acid, ester, halide, hydroxamate, hydroxy, ketone, nitro, silyl, sulfo-oxo, sulfonyl, sulfone, sulfoxide, or thiol as described herein. A biaryl group is a specific type of aryl group and is included in the definition of aryl. Biaryl refers to two aryl groups that are bound together via a fused ring structure, as in naphthalene, or are attached via one or more carbon-carbon bonds, as in biphenyl.

Suitable electron withdrawing groups and electron releasing groups are generally known in the art. Preferred electron withdrawing groups include nitro, carboxylic acid, esters, for example loweralkyl esters, and cyano. Preferred electron releasing groups include branched and straight chain alkyl groups, for example, methyl, ethyl, propyl, isopropyl, butyl, isobutyl, and tert-butyl. Other preferred electron releasing groups include alkoxy, for example methoxy and ethoxy. Other preferred electron releasing groups include thioalkyl. Still other preferred electron releasing groups include amines, for example —NH₂, and NH(loweralkyl), and N(loweralkyl)₂.

Preferred oxygen scavengers of Formula (I) and (II) are disclosed in U.S. Patent Application Publication No. 20080277622, Deshpande et al. “Oxygen Scavenging Molecules, Articles Containing Same, And Methods of Their Use,” which is incorporated herein by this reference for its teaching of oxygen scavengers, their preparation, and their use as oxygen scavenging materials.

In a further aspect, the oxygen scavenger is polymeric or copolymeric and comprises a structure of Formula III:

wherein m is a positive integer greater than 10; wherein n is an integer from 1 to 6; and wherein R³ is H or C1-C4 alkyl. The C1-C4 alkyl group can be substituted or unsubstituted methyl, ethyl, propyl, butyl, isopropyl, or isobutyl. In a further aspect, R³ is H. In one aspect, n is 4. One example of a compound of Formula III is MXD6 (available commercially, e.g., from Mitsubishi Gas Chemicals of Japan). MXD6 is a polymer produced by condensation of meta-xylylene diamine and adipic acid. Compounds of Formula III can be obtained from commercial sources or be prepared by polymerization methods known in the art. Suitable grades include HB-5299 from EMS Grivory; 6001, 6003, 6007 and 6121 from Mitsubishi Gas and Chemical Company.

In one aspect, the oxygen scavenger has a structure of Formula I: the oxygen scavenger has a structure represented by a formula:

E-(L-E)_(x)

wherein x is 0, 1, or 2; wherein E has a structure of Formula IV or Formula V:

wherein L is a linking group of the formula —(O—R²¹)_(z)—O—, —(NH—R²¹)_(z)—NH—, —(NH—C(═O)R²²)_(t)—NH, —NH—R²⁵—NH(C(═O)R²⁶NHR²⁵NH)_(u)—, —(O—R²³—O—R²⁴—C(═O)_(z)—O)— where L is attached to a carbon atom of at least one Ar in Formula IV or where R¹² and/or R¹³ of Formula V is L; wherein Ar is aryl or heteroaryl; wherein R¹, R², and R¹¹ are each independently, H, C₁-C₁₂ alkyl, C₁-C₆ alkoxy, C₆-C₂₀ aryloxy, hydroxy, C₂-C₆ alkenyl, NR¹⁹R²⁰, acetyl, nitro, glyceryl, carbohydrate, —C(═O)H, L, or two R¹ or two R² groups can form a group of the formula —O‘3R¹⁸—O; wherein R³, R⁴, R¹⁴, and R¹⁵ are each H; R⁵ to R¹⁰ and R¹⁶, and R¹⁷ are each, independently, H or C₁-C₃ alkyl; R¹² and R¹³ are each, independently, H, C₁-C₆ alkyl, C₆-C₂₀ aryl, C₁-C₆ alkoxy, or L; wherein R¹⁸ is C₂-C₆ alkyl; R¹⁹ and R²⁰ are each, independently, H, C₁-C₆ alkyl, or C₆-C₂₀ aryl; wherein R², and R²⁴ are each, independently, C₁-C₆ alkyl; wherein R²², R²³, R²⁵ and R²⁶ are each, independently, C₁-C₆ alkyl or C₆-C₂₀ aryl; wherein n and p are independently 0 or an integer from 1 to 5; wherein q is 0 or an integer from 1 to 4; wherein s and z are independently 1, 2, or 3; and wherein t and u are independently 1 or 2.

In a further aspect, E has a structure of Formula IV:

In a further aspect, the oxygen scavenger has a structure represented by a formula:

In a further aspect, n and p are each 0, 1, or 2 and R1 and R² are each independently H, C₁-C₄ alkyl, hydroxy, C₁-C₃ alkoxy, or carbohydrate. In a further aspect, R¹ and R² are each independently H, methyl, ethyl, hydroxy, methoxy, ethoxy, or glucose. In a further aspect, R⁵ to R¹⁰ are each H. In a further aspect, R¹ and R² are each H. In a further aspect, the oxygen scavenger has a structure represented by a formula:

In a further aspect, E has a structure of Formula V:

In a further aspect, the oxygen scavenger has a structure represented by a formula:

In a further aspect, R¹⁶ and R¹⁷ are H. In a further aspect, each R¹¹ is independently H, C₁-C₄ alkyl, hydroxy, or C₁-C₃ alkoxy, or carbohydrate. In a further aspect, each R¹¹ is independently H, methyl, ethyl, hydroxy, methoxy, or ethoxy. In a further aspect, the oxygen scavenger has a structure represented by a formula:

Preferred oxygen scavengers of Formula (IV) and (V) are disclosed in U.S. Patent Application Publication No. 20060180790, Deshpande et al. “Oxygen scavenging compositions and packaging comprising said compositions,” which is incorporated herein by this reference for its teaching of oxygen scavengers, their preparation, and their use as oxygen scavenging materials.

In other aspects, the oxygen scavenger can be any one or more of the conventionally known polybutadiene based oxygen scavengers. Exemplary and non-limiting examples of commercially available polybutadiene based oxygen scavengers include the Amosorb® line of oxygen scavengers available from ColorMatrix of Berea, Ohio, USA.

Compounds

Disclosed herein are compounds capable of being formulated with one or more base polymers wherein the compounds when formulated with the one or more base polymers to provide a polymer composition that can serve as a barrier to slow, retard, or stop the flow of carbon dioxide or water vapor or other gaseous/organoleptic transport through the polymer composition.

The compositions comprise from about 0.10% to about 10% weight percent of the compound. In one embodiment the compositions comprise from about 0.5% to about 10% by weight of an compound. In another embodiment the compositions comprise from about 1% to about 5% by weight of an compound. In a further embodiment the compositions comprise from about 0.1% to about 1% by weight of an compound. In a still further embodiment the compositions comprise from about 0.1% to about 5% by weight of an compound. In a yet further embodiment the compositions comprise from about 3% to about 10% by weight of an compound. In another further embodiment the compositions comprise from about 5% to about 10% by weight of an compound. In a yet another embodiment the compositions comprise from about 2% to about 7% by weight of an compound.

The compounds that can be formulated with the base polymer have the formula:

wherein le to le are each independently chosen from:

-   -   i) hydrogen;     -   ii) C₁-C₁₂ substituted or unsubstituted linear, branched, or         cyclic alkyl;     -   iii) C₂-C₁₂ substituted or unsubstituted linear, branched, or         cyclic alkenyl;     -   iv) C₂-C₁₂ substituted or unsubstituted linear or branched         alkynyl;     -   v) C₆ or C₁₀ substituted or unsubstituted aryl;     -   vi) C₁-C₉ substituted or unsubstituted heterocyclic;     -   vii) C₁-C₁₁ substituted or unsubstituted heteroaryl;     -   viii) —[C(R^(10a))(R^(10b))]_(y)OR¹¹;         -   wherein R¹¹ is chosen from:         -   a) —H;         -   b) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclic alkyl or C₁-C₁₂ substituted or unsubstituted linear,             branched, or cyclic haloalkyl;         -   c) C₆ or C₁₀ substituted or unsubstituted aryl or C₇-C₂₀             alkylenearyl;         -   d) C₁-C₉ substituted or unsubstituted heterocyclic; and         -   e) C₁-C₁₁ substituted or unsubstituted heteroaryl;     -   ix) —[C(R^(10a))(R^(10b))]_(y)N(R^(12a))(R^(12b));         -   wherein R^(12a) and R^(12b) are each independently chosen             from:         -   a) —H;         -   b) —OR¹³;         -   R¹³ is hydrogen or C₁-C₄ linear alkyl;         -   c) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclic alkyl;         -   d) C₆ or C₁₀ substituted or unsubstituted aryl;         -   e) C₁-C₉ substituted or unsubstituted heterocyclic;         -   f) C₁-C₁₁ substituted or unsubstituted heteroaryl; and         -   g) R^(12a) and R^(12b) can be taken together to form a             substituted or unsubstituted ring having from 3 to 10 carbon             atoms and from 0 to 3 heteroatoms chosen from oxygen,             nitrogen, and sulfur;     -   x) —[C(R^(10a))(R^(10b))]_(y)C(O)R¹⁴;         -   wherein R¹⁴ is chosen from:         -   a) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclicalkyl;         -   b) —OR¹⁵;             -   wherein R¹⁵ is hydrogen, substituted or unsubstituted                 C₁-C₄ linear alkyl, C₆ or C₁₀ substituted or                 unsubstituted aryl, C_(l)-C₉ substituted or                 unsubstituted heterocyclic, C₁-C₁₁ substituted or                 unsubstituted heteroaryl; and         -   c) —N(R^(16a))(R^(16b));             -   wherein R^(16a) and R^(16b) are each independently                 hydrogen, C₁-C₁₂ substituted or unsubstituted linear,                 branched, or cyclic alkyl; C₆ or C₁₀ substituted or                 unsubstituted aryl; C₁-C₉ substituted or unsubstituted                 heterocyclic; C₁-C₁₁ substituted or unsubstituted                 heteroaryl; or R^(16a) and R^(16b) can be taken together                 to form a substituted or unsubstituted ring having from                 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen                 from oxygen, nitrogen, and sulfur;     -   xi) —[C(R^(10a))(R^(10b))]_(y)OC(O)R¹⁷;         -   wherein R¹⁷ is chosen from:         -   a) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclic alkyl; and         -   b) —N(R^(18a))(R^(18b));             -   R^(18a) and R^(18b) are each independently hydrogen,                 C₁-C₁₂ substituted or unsubstituted linear, branched, or                 cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted                 aryl; C₁-C₉ substituted or unsubstituted heterocyclic;                 C₁-C₁₁ substituted or unsubstituted heteroaryl; or                 R^(18a) and R^(18b) can be taken together to form a                 substituted or unsubstituted ring having from 3 to 10                 carbon atoms and from 0 to 3 heteroatoms chosen from                 oxygen, nitrogen, and sulfur;     -   xii) —[C(R^(10a))(R^(10b))]_(y)NR¹⁹C(O)R²⁰;         -   wherein R¹⁸ is chosen from:         -   a) —H; and         -   b) C₁-C₄ substituted or unsubstituted linear, branched, or             cyclicalkyl;         -   wherein R²⁰ is chosen from:         -   a) C₁-C₁₂ substituted or unsubstituted linear, branched, or             cyclic alkyl; and         -   b) —N(R^(21a))(R^(21b));             -   R^(21a) and R^(21b) are each independently hydrogen,                 C₁-C₁₂ substituted or unsubstituted linear, branched, or                 cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted                 aryl; C₁-C₉ substituted or unsubstituted heterocyclic;                 C₁-C₁₁ substituted or unsubstituted heteroaryl; or                 R^(21a) and R^(21b) can be taken together to form a                 substituted or unsubstituted ring having from 3 to 10                 carbon atoms and from 0 to 3 heteroatoms chosen from                 oxygen, nitrogen, and sulfur;     -   xiii) —[C(R^(10a))(R^(10b))]_(y)CN;     -   xiv) —[C(R^(10a))(R^(10b))]_(y)NO₂;     -   xv) —[C(R^(10a))(R^(10b))]_(y)SO₂R²²;         -   R²² is hydrogen, hydroxyl, substituted or unsubstituted             C₁-C₄ linear or branched alkyl; substituted or unsubstituted             C₆, C₁₀, or C₁₄ aryl; C₇-C₁₅ alkylenearyl; C₁-C₉ substituted             or unsubstituted heterocyclic; or C₁-C₁₁ substituted or             unsubstituted heteroaryl; and     -   xvi) halogen;     -   xvii) —[C(R^(10a))(R^(10b))]_(y)(CH_(j′)X_(k′))_(h)CH_(j)X_(k);         wherein X is halogen, the index j is an integer from 0 to 2, the         index k is an integer from 1 to 3, j+k=3; the index j′ is an         integer from 0 to 2, the index k′ is and integer from 0 to 2,         j′+k′=2; the index h is from 0 to 5;         -   R^(10a) and R^(10b) are each independently hydrogen or C₁-C₄             alkyl; and the index y is from 0 to 5;         -   R¹ and R⁸ can be taken together to from a 5 to 7 member ring             containing from 3 to 7 carbon atoms and from 0 to 2             heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein             one or more of the carbon atoms can be substituted,             unsubstituted, or a carbonyl unit.

As described herein above, the various units that comprise R¹ to R⁸ can be substituted by one or more units independently chosen from:

-   -   i) C₁-C₁₂ linear, branched, or cyclic alkyl, alkenyl, and         alkynyl;     -   ii) C₁-C₁₂ linear, branched, or cyclic alkoxy, alkenyloxy, and         alkynyloxy;     -   iii) C₁-C₁₂ linear, branched, or cyclic haloalkyl, haloalkenyl,         and haloalkynyl;     -   iv) C₆ or C₁₀ aryl;     -   v) C₆ or C₁₀ alkylenearyl;     -   vi) C₁-C₉ heterocyclic rings;     -   vii) C₁-C₉ heteroaryl rings;     -   viii) —(CR^(102a)R^(102b))_(z)OR¹⁰¹;     -   ix) —(CR^(102a)R^(102b))_(z)C(O)R¹⁰¹;     -   x) —(CR^(102a)R^(102b))_(z)C(O)OR¹⁰¹;     -   xi) —(CR^(102a)R^(102b))_(z)C(O)N(R¹⁰¹)₂;     -   xii) —(CR^(102a)R^(102b))_(z)N(R101)₂;     -   xiii) halogen;     -   xiv) —(CR^(102a)R^(102b))_(z)CN;     -   xv) —(CR^(102a)R^(102b))_(z)NO₂;     -   xvi) —CH_(j)X_(k); wherein X is halogen, the index j is an         integer from 0 to 2, j+k=3; for example,     -   xvii) —(CR^(102a)R^(102b))_(z)SR¹⁰¹;     -   xviii) —(CR^(102a)R^(102b))_(z)SO₂R¹⁰¹ and     -   xix) —(CR^(102a)R^(102b))_(z)SO₃R¹⁰¹;     -   wherein each R¹⁰¹ is independently hydrogen, substituted or         unsubstituted C₁-C₆ linear, branched, or cyclic alkyl, phenyl,         benzyl, heterocyclic, or heteroaryl; or two R¹⁰¹ units can be         taken together to form a ring comprising 3-7 atoms; R^(102a) and         R^(102b) are each independently hydrogen or C₁-C₄ linear or         branched alkyl; the index z is from 0 to 4.

One aspect of the present disclosure relates to compounds wherein R¹ and R⁸ can be taken together to from a 5 to 7 member ring containing from 3 to 7 carbon atoms and from 0 to 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms can be substituted, unsubstituted, or a carbonyl unit.

One embodiment of this aspect relates to compounds wherein R¹ and R⁸ are taken together to form a 6-member ring, for example, compounds chosen from:

-   -   i) benzo[de]isochromen-1(3H)-one having the formula:

-   -   ii) 1H-henzo[de]isoquinoline-1,3(2H)-dione having the formula:

-   -   iii) 2,3-dihydro-1H-benzo[de]isoquinolin-1-one having the         formula:

and

-   -   iv) benzo[de]-isochromene-1,3-dione having the formula:

Another aspect of the present disclosure as it relates to compounds includes compounds having the formula:

-   -   wherein R¹ and R⁸ are each independently:     -   i) hydrogen; or     -   ii) —C(O)R¹⁴;         wherein R¹⁴ is —OR¹⁵ or —N(R^(16a))(R^(16b)); R¹⁵ is hydrogen or         methyl; R^(16a) and R^(16b) are each independently hydrogen or         methyl. A non-limiting example of this aspect is         naphthalene-1,8-dicarboxyamide having the formula:

For example, if a compound benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) is added to PET, the molecular size of benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) is just smaller than the free volume of PET at room temperature. A typical PET resin used in bottles has a molecular weight of 28,000. Free volume of PET at room temperature is around 1301 (Angstrom)³ (Reference: Polyakova, A, et. al., Journal of Polymer Science: Part B: Polymer Physics, Vol 39, pages 1889-1899, year 2001). Molecular volume of benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) and 1H-henzo[de]isoquinoline-1,3(2H)-dione (1,8-Napthalimide) is 872 (Angstrom)³ and 889 (Angstrom)³ (Reference: Lieh Nguyen Shok and G. A. Gol'der, Translated from Zhurnal Strukturnoi Khimii, Vol. 11, No. 5, pp. 939-940, September-October 1970). As seen from the molecular volume numbers, it is clear that benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) and 1H-henzo[de]isoquinoline-1,3(2H)-dione (1,8-Napthalimide) molecules can fit inside the free volume of individual PET chains and reduce the free volume of PET by as much as 68%. This reduction in free volume due to incorporation of additives described above increase the hop distance for CO₂ diffusion through PET, thereby reducing the CO₂ permeation rate and increasing shelf life of carbonated soft drink (CSD) and beer bottles.

Various methods exist for making the composition. In one aspect, the composition can be made by mixing the base polymer with the oxygen scavenger and the compound. In another aspect, the composition can be made by mixing the base polymer with the compound. In some aspects, the base polymer, the oxygen scavenger and the compound are mixed by tumbling in a hopper. Other optional ingredients can be added during this mixing process or added to the mixture after the aforementioned mixing or to an individual component prior to the aforementioned mixing step.

When melt processing is desired for the composition, the composition can also be made by adding each ingredient separately and mixing the ingredients just prior melt processing the composition to form an article. In some embodiments, the mixing can be just prior to the melt process zone. In other embodiments, one or more ingredients can be premixed in a separate step prior to bringing all of the ingredients together.

In some aspects, the compound can be added neat or in a carrier (such as a liquid or wax) to an extruder or other device for making the article, or the compound can be present in a concentrate or carrier with the oxygen scavenger, in a concentrate or carrier with the base polymer, or in a concentrate or carrier with a base polymer/oxygen scavenger blend. It is desirable that the addition of the compound does not substantially increase the intrinsic viscosity of the melt in the melt processing zone. Thus, compounds can be added in two or more stages, such as once during the melt phase for the production of the base polymer and again once more to the melting zone for making the article.

The melt blend of base polymer, oxygen scavenger, and compound can also be prepared by adding the components at the throat of an injection molding machine that: (i) produces a preform that can be stretch blow molded into the shape of the container, (ii) produces a film that can be oriented into a packaging film, (iii) produces a sheet that can be thermoformed into a food tray, or (iv) produces an injection molded container. The mixing section of the extruder should be of a design to produce a homogeneous blend. Such process steps work well for forming carbonated soft drink, water or beer bottles, packaging films and thermoformed trays. The present invention can be employed in any of the conventional known processes for producing a polymeric container, film, tray, or other article that would benefit from oxygen scavenging.

Articles

Various articles can be prepared from the disclosed compositions. Thus, the articles prepared from the compositions will also have the composition present in the article. Suitable articles include vessels and films, such as flexible sheet films, flexible bags, pouches, semi-rigid and rigid containers such as bottles (e.g. PET bottles) or combinations thereof. Typical flexible films and bags include those used to package various food items and can be made up of one or a multiplicity of layers to form the overall film or bag-like packaging material. The disclosed compositions can be used in one, some or all of the layers of such packaging material.

Specific articles include preforms, containers and films for packaging of food, beverages, cosmetics, pharmaceuticals, and personal care products where a high carbon dioxide or moisture or organoleptic barrier is needed. Examples of beverage containers are bottles for holding water and carbonated soft drinks, and the invention is particularly useful in bottle applications containing juices, sport drinks, beer or any other beverage where loss of carbon dioxide detrimentally affects the flavor, fragrance, performance (e.g., vitamin degradation). The compositions can also be useful as a sheet for thermoforming into rigid packages and films for flexible structures to deliver organoleptic and moisture barrier. Rigid packages include food trays and lids. The compositions can also be used in the manufacture of cosmetic containers and containers for pharmaceuticals or medical devices.

Other suitable articles include rigid or semi-rigid articles including plastic, such as those utilized for juices, soft drinks, as well as thermoformed trays or cup normally having thickness in the range of from 100 to 1000 micrometers. The walls of such articles can comprise single or multiple layers of materials. The article can also take the form of a bottle or can, or a crown, cap, crown or cap liner, plastisol or gasket (if the part is made up of PET). As a liner, the composition can be extruded as a film along with the rigid article itself, e.g., by coextrusion, extrusion coating, or an extrusion lamination process, so as to form the liner in situ during article production; or alternatively can be adhered by heat and/or pressure, by adhesive, or by any other suitable method (as long as the liner is comprised of PET).

Besides articles applicable for packaging food and beverage, articles for packaging other carbon dioxide-sensitive products can also benefit from the present invention. Such products would include modified atmosphere packaging of fruits and vegetables, medical devices and the like.

In a further aspect, the composition can be used as a master batch for blending with a polymer or a polymer containing component. In such compositions, the concentration of the compound will be high enough to allow for the final blended product to have suitable amounts of these components. The master batch can also contain an amount of the base polymer with which the master batch is blended.

The articles can be made by various methods known in the art. Generally, the articles are prepared by melt processing methods (i.e., a melt of the composition). Such processes generally include injection molding, stretch blow molding, extrusion, thermoforming, extrusion blow molding, and (specifically for multilayer structures) co-extrusion and lamination using adhesive tie layers. Orientation, e.g., by stretch blow molding, of the polymer can be used with phthalate polyesters because of the known mechanical advantages that result.

The melt processing zone for making the article can be operated under customary conditions effective for making the intended articles, such as preforms, bottles, trays, and other articles mentioned above. In one aspect, such conditions are effective to process the melt without substantially increasing the intrinsic viscosity of the melt and which are ineffective at promoting transesterification reactions. In some preferred aspects, suitable operating conditions effective to establish a physical blend of the base polymer, oxidizable organic component, and transition metal are temperatures in the melt processing zone within a range of about 250° C. to about 300° C. at a total cycle time of less than about 6 minutes, and typically without the application of vacuum and under a positive pressure ranging from about 0 psig (pound-force per square inch gauge) to about 900 psig. In some embodiments, the residence time of the melt on the screw can range from about 1 to about 6 minutes.

EXAMPLE 1

A 21.6 gram polyethylene terephthalate preform comprising compounds as disclosed herein was prepared on a 2-cavity Husky LX 160 injection molding machine under standard injection conditions. The following table (Table 1) compares the examples according to the present disclosure with samples comprising the disclosed compounds and a sample wherein caffeine substitutes for the disclosed compounds.

TABLE 1 benzo[de]- benzo[de]iso- Run Caf- isochromene- quinoline-1,3- No. PET^(1,2) feine 1,3-dione dione 6821-1 Parastar 7000 ™ — — — 6696-2 Parastar 7000 ™  5% — — 6696-4 Parastar 7000 ™ — 2.5% — 6696-3 Parastar 7000 ™ — — 2.5% 6821-2 Parastar 7000 ™ 10% — — 6821-4 Parastar 7000 ™ —  5% — 6821-3 Parastar 7000 ™ — —  5% Parastar 7000 is a commercially available PEI' resin available from Eastman Chemical Co., Kingsport, Tenn., USA.

The preforms were blown into a 12 oz. carbonated soft drink (CSD) container on Sidel's SBO 2/3 blow molding machine. The 12 oz. CSD bottles were then tested for CO₂ retention using Quantiperm.Model 504 (manufactured by Quantiperm, LLC). This instrument allows direct, real-time measurement of CO₂ loss from plastic bottles. Prior to testing the bottles are filled with carbonated water till 4.2 gas volumes of CO₂ for approximately one week in the preconditioning phase. After preconditioning phase is complete, the CO₂ efflux through the bottle wall is at a substantially constant rate. The Quantiperm instrument measures this steady state loss rate rapidly and directly. The real time loss rates are combined with the driving force (CO₂ partial pressure within the packages) to make accurate shelf life estimation for carbonated packages. A barrier improvement factor (BIF) can be determined by taking a ratio of the time taken for 20% CO₂ loss for the control package and the test package.

FIGS. 1, 2(a), and 2(b) show CO₂ loss as a function of time for variables 6821-1, 6821-2, 6821-3 and 6821-4, as measured by Quantiperm Model 504. Addition of 5% benzo[de]isochromene-1,3-dione and 5% benzo[de]isoquinoline-1,3-dione to PET reduces the rate of CO₂ loss, with a BIF of 1.67X over PET. Variable 6821-2 did not offer as much improvement (BIF =1.1X) as Variables 6821-3 and 6821-4. As seen from FIG. 3, 6696-2 did not offer a substantial BIF over PET, but 6696-3 and 6696-4 showed improved performance, with a BIF of ˜1.2×.

EXAMPLE 2

A 35.5 gram PET preform for a 16 oz. stock beer bottle comprising compounds as disclosed herein was prepared on a 2-cavity Husky LX 160 injection molding machine under standard injection conditions. The following table (Table 2) compares the examples according to the present disclosure with samples comprising the disclosed compounds.

TABLE 2 Wt % of Run # PET used Additive used additive 8139-1 Parastar 7000 None (Control) 8139-2 Parastar 7000 ColorMatrix Process Aid 1% 80-561-1 8139-3 Parastar 7000 ColorMatrix Process Aid 0.6%  80-561-1 8139-4 Parastar 7000 Croda's Atmer 7150 5% 8139-5 Parastar 7000 Techmer 13350 5% 8139-6 Parastar 7000 1,8-Naphthalic Anhydride 5% (benzo[de]-isochromene- 1,3-dione) 8139-7 Parastar 7000 1,8-Naphthalic Anhydride 4% ColorMatrix Process Aid 0.4%  80-561-1

The preforms were blown into 16 oz. beer bottles on Sidel's SBO 2/3 blow molding machine. The preform heating zone profile for SBO 2/3 are shown in Table 3 below.

TABLE 3 Bulb distance % Power from preform from 2000 support ledge Oven 1 Oven 2 Oven 3 Zone W lamp (mm) ON/OFF ON/OFF ON/OFF 1 98% 7.5 ON ON ON 2 88% 22.5 ON ON ON 3 46% 37.5 OFF ON OFF 4 40% 52.5 ON ON OFF 5 45% 67.5 OFF ON ON 6 45% 82.5 OFF OFF ON 7 51% 97.5 ON ON ON

The preforms were blown on a cold mold (at 55 F) by using a 12 mm diameter stretch rod, 40 bar air pressure and at a machine speed of 1500 bottles/hour. The preform heat setting (shown in Table 3) resulted in INT of 103 F as measured by infrared thermometer aimed at zone 3 of the preform coming out of the heating zone.

The 16 oz. beer bottles were then tested for CO₂ retention, O₂ Transmission Rate (OTR) and WVTR (water vapor transmission rate) to determine the effect of various additives on gas permeation.

A brief description of the apparatus (Quantiperm Model 504) used to measure CO₂ transmission rate is shown in Example 1. FIGS. 4 and 5 show CO₂ loss as a function of time for variables 8139-1, 8139-2, 8139-3, 8139-4, 8139-5, 8139-6 and 8139-7, as measured by Quantiperm Model 504. For beer bottles, shelf life is determined by measuring the time required for 15% CO₂ loss from initial carbonation levels. The shelf life and CO₂ BIF for different variables is shown in Table 4 below:

TABLE 4 Shelf life OTR cc/pkg/day Example 2, (weeks) Measured CO₂ (measured O₂ Run # by Quantiperm BIF by Iliop) BIF 8139-1 9   1X 0.0309   1X (CONTROL) 8139-2 9   1X 0.0285 1.08X 8139-3 11 1.22X 0.0284 1.09X 8139-4 9   1X 0.0307   1X 8139-5 10 1.11 0.0296 1.04X 8139-6 13 1.44X 0.0199 1.55X 8139-7 14 1.56X 0.0208 1.49X

Addition of 4% benzo[de]isochromene-1,3-dione and 0.4% Fatty Acid Ester such as ColorMatrix Process Aid 80-561-1 to PET (Run 8139-7) reduces the rate of CO₂ loss, with a BIF of ˜1.56× over PET. Variable 8139-2 and 8139-4 did not offer any improvement in CO₂ barrier—indicating the use of fatty acid esters by themselves have negligible effect on reducing the CO₂ permeation through PET bottle. Addition of 5% benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) to PET (Run 8139-6) did increase the shelf life by 1.44× over Control PET beer bottle. This result is similar to the result described in Example 1.

In addition to CO2 permeation rate measurements, the bottles of Example 2 were tested for O₂ transmission rates (OTR) using Illiop. The OTR data show that addition of benzo[de]-isochromene-1,3-dione (1,8-Naphthalic Anhydride) to PET (in Run 8139-6 and 8139-7) resulted in reduction in OTR along with a reduction of CO2 TR (as seen from an increase in shelf life).

While particular embodiments of the present disclosure have been illustrated and described, it would be obvious to those skilled in the art that various other changes and modifications can be made without departing from the spirit and scope of the disclosure. It is therefore intended to cover in the appended claims all such changes and modifications that are within the scope of this disclosure. 

1. A polymer composition, comprising: a) a base polymer; and b) from about 0.1% to about 10% by weight of a compound having the formula:

 wherein R^(l) to R⁸ are each independently chosen from: i) hydrogen; ii) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; iii) C₂-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkenyl; iv) C₂-C₁₂ substituted or unsubstituted linear or branched alkynyl; v) C₆ or C₁₀ substituted or unsubstituted aryl; vi) C₁-C₉ substituted or unsubstituted heterocyclic; vii) C₁-C₁₁ substituted or unsubstituted heteroaryl; viii) —[C(R^(10a))(R^(10b))]_(y)OR¹¹; wherein R¹¹ is chosen from: a) —H; b) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl or C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic haloalkyl; c) C₆ or C₁₀ substituted or unsubstituted aryl or C₇-C₂₀ alkylenearyl; d) C₁-C₉ substituted or unsubstituted heterocyclic; and e) C₁-C₁₁ substituted or unsubstituted heteroaryl; ix) —[C(R^(10a))(R^(10b))]_(y)N(R^(12a))(R^(12b)); wherein R^(12a) and R^(12b) are each independently chosen from: a) —H; b) —OR¹³; R¹³ is hydrogen or C₁-C4 linear alkyl; c) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; d) C₆ or C₁₀ substituted or unsubstituted aryl; e) C₁-C₉ substituted or unsubstituted heterocyclic; f) C₁-C₁₁ substituted or unsubstituted heteroaryl; and g) R^(12a) and R^(12b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; x) —[C(R^(10a))(R^(10b))]_(y)C(O)R¹⁴; wherein R¹⁴ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; b) —OR¹⁵; wherein R¹⁵ is hydrogen, substituted or unsubstituted C₁-C₄ linear alkyl, C₆ or C₁₀ substituted or unsubstituted aryl, C_(l)-C₉ substituted or unsubstituted heterocyclic, C₁-C₁₁ substituted or unsubstituted heteroaryl; and c) —N(R^(16a))(R^(16b)); wherein R^(16a) and R^(16b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(16a) and R^(16b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xi) —[C(R^(10a))(R^(10b))]_(y)OC(O)R¹⁷; wherein R¹⁷ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; and b) —N(R^(18a))(R^(18b)); R^(18a) and R^(18b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(18a) and R^(18b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xii) —[C(R^(10a))(R^(10b))]_(y)NR¹⁹C(O)R²⁰; wherein R¹⁸ is chosen from: a) —H; and b) C₁-C₄ substituted or unsubstituted linear, branched, or cyclic alkyl; wherein R²⁰ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; and b) —N(R^(21a))(R^(21b)); R^(21a) and R^(21b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(21a) and R^(21b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xiii) —[C(R^(10a))(R^(10b))]_(y)CN; xiv) —[C(R^(10a))(R^(10b))]_(y)NO₂; xv) —[C(R^(10a))(R^(10b))]_(y)SO₂R²²; R²² is hydrogen, hydroxyl, substituted or unsubstituted C₁-C₄ linear or branched alkyl; substituted or unsubstituted C₆, C₁₀, or C₁₄ aryl; C₇-C₁₅ alkylenearyl; C₁-C₉ substituted or unsubstituted heterocyclic; or C₁-C₁₁ substituted or unsubstituted heteroaryl; and xvi) halogen; xvii) —[C(R^(10a))(R^(10b))]_(y)(CH_(j′)X_(k′))_(h)CH_(j)X_(k); wherein X is halogen, the index j is an integer from 0 to 2, the index k is an integer from 1 to 3, j+k=3; the index j′ is an integer from 0 to 2, the index k′ is and integer from 0 to 2, j′+k′=2; the index h is from 0 to 5; R^(10a) and R^(10b) are each independently hydrogen or C₁-C₄ alkyl; and the index y is from 0 to 5; R¹ and R⁸ can be taken together to from a 5 to 7 member ring containing from 3 to 7 carbon atoms and from 0 to 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms can be substituted, unsubstituted, or a carbonyl unit.
 2. A composition according to claim 1, wherein the substitutions are each independently chosen from: i) C₁-C₁₂ linear, branched, or cyclic alkyl, alkenyl, and alkynyl; ii) C₁-C₁₂ linear, branched, or cyclic alkoxy, alkenyloxy, and alkynyloxy; iii) C₁-C₁₂ linear, branched, or cyclic haloalkyl, haloalkenyl, and haloalkynyl; iv) C₆ or C₁₀ aryl; v) C₆ or C₁₀ alkylenearyl; vi) C₁-C₉ heterocyclic rings; vii) C₁-C₉ heteroaryl rings; viii) —(CR^(102a)R^(102b))_(z)OR¹⁰¹; ix) —(CR^(102a)R^(102b))_(z)C(O)R¹⁰¹; x) —(CR^(102a)R^(102b))_(z)C(O)OR¹⁰¹; xi) —(CR^(102a)R^(102b))_(z)C(O)N(R¹⁰¹)₂; xii) —(CR^(102a)R^(102b))_(z)N(R101)₂; xiii) halogen; xiv) —(CR^(102a)R^(102b))_(z)CN; xv) —(CR^(102a)R^(102b))_(z)NO₂; xvi) —CH_(j)X_(k); wherein X is halogen, the index j is an integer from 0 to 2, j+k=3; for example, xvii) —(CR^(102a)R^(102b))_(z)SR¹⁰¹; xviii) —(CR^(102a)R^(102b))^(z)SO₂R¹⁰¹ and xix) —(CR^(102a)R^(102b))_(z)SO₃R¹⁰¹; wherein each R¹⁰¹ is independently hydrogen, substituted or unsubstituted C₁-C₆ linear, branched, or cyclic alkyl, phenyl, benzyl, heterocyclic, or heteroaryl; or two R¹⁰¹ units can be taken together to form a ring comprising 3-7 atoms; R^(102a) and R^(102b) are each independently hydrogen or C₁-C₄ linear or branched alkyl; the index z is from 0 to
 4. 3. The composition according to claim 1, wherein R² to R⁷ are each hydrogen.
 4. The composition according to claim 1, wherein R¹ and R⁸ can be taken together to from 6 member ring containing from 4 to 5 carbon atoms and 1 or 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms is a carbonyl unit.
 5. The composition according to claim 1, wherein the compound is chosen from: i) benzo[d]isochromen-1(3H)-one having the formula:

ii) 1H-henzo[d]isoquinoline-1,3(2H)-dione having the formula:

and iii) 2,3-dihydro-1H-benzo[de]isoquinolin-1-one having the formula:


6. The composition according to claim 1, wherein the compound is benzo[de]-isochromene-1,3-dione having the formula:


7. The composition according to claim 1, wherein the compound has the formula:

R¹ and R⁸ are each independently: i) hydrogen; or ii) —C(O)R¹⁴; wherein R¹⁴ is —OR¹⁵ or —N(R^(16a))(R^(16b)); R¹⁵ is hydrogen or methyl; R^(16a) and R^(16b) are each independently hydrogen or methyl.
 8. The composition according to claim 1, wherein the compound is naphthalene-1,8-dicarobxamide having the formula:


9. The composition according to claim 1, wherein the oxygen scavenger is an N-allylic amine or N-benzylic amide.
 10. The composition according to claim 1, wherein the base polymer comprises a polyester or a polypropylene.
 11. (canceled)
 12. (canceled)
 13. (canceled)
 14. (canceled)
 15. (canceled)
 16. An article of manufacture, comprising: a) a base polymer; b) from about 0.1% to about 10% by weight of a compound having the formula:

 wherein R^(l) to R⁸ are each independently chosen from: i) hydrogen; ii) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; iii) C₂-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkenyl; iv) C₂-C₁₂ substituted or unsubstituted linear or branched alkynyl; v) C₆ or C₁₀ substituted or unsubstituted aryl; vi) C₁-C₉ substituted or unsubstituted heterocyclic; vii) C₁-C₁₁ substituted or unsubstituted heteroaryl; viii) —[C(R^(10a))(R^(10b))]_(y)OR¹¹; wherein R¹¹ is chosen from: a) —H; b) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl or C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic haloalkyl; c) C₆ or C₁₀ substituted or unsubstituted aryl or C₇-C₂₀ alkylenearyl; d) C₁-C₉ substituted or unsubstituted heterocyclic; and e) C₁-C₁₁ substituted or unsubstituted heteroaryl; ix) —[C(R^(10a))(R^(10b))]_(y)N(R^(12a))(R^(12b)); wherein R^(12a) and R^(12b) are each independently chosen from: a) —H; b) —OR¹³; R¹³ is hydrogen or C₁-C4 linear alkyl; c) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; d) C₆ or C₁₀ substituted or unsubstituted aryl; e) C₁-C₉ substituted or unsubstituted heterocyclic; f) C₁-C₁₁ substituted or unsubstituted heteroaryl; and g) R^(12a) and R^(12b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; x) —[C(R^(10a))(R^(10b))]_(y)C(O)R¹⁴; wherein R¹⁴ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; b) —OR¹⁵; wherein R¹⁵ is hydrogen, substituted or unsubstituted C₁-C₄ linear alkyl, C₆ or C₁₀ substituted or unsubstituted aryl, C_(l)-C₉ substituted or unsubstituted heterocyclic, C₁-C₁₁ substituted or unsubstituted heteroaryl; and c) —N(R^(16a))(R^(16b)); wherein R^(16a) and R^(16b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(16a) and R^(16b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xi) —[C(R^(10a))(R^(10b))]_(y)OC(O)R¹⁷; wherein R¹⁷ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; and b) —N(R^(18a))(R^(18b)); R^(18a) and R^(18b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(18a) and R^(18b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xii) —[C(R^(10a))(R^(10b))]_(y)NR¹⁹C(O)R²⁰; wherein R¹⁸ is chosen from: a) —H; and b) C₁-C₄ substituted or unsubstituted linear, branched, or cyclic alkyl; wherein R²⁰ is chosen from: a) C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; and b) —N(R^(21a))(R^(21b)); R^(21a) and R^(21b) are each independently hydrogen, C₁-C₁₂ substituted or unsubstituted linear, branched, or cyclic alkyl; C₆ or C₁₀ substituted or unsubstituted aryl; C₁-C₉ substituted or unsubstituted heterocyclic; C₁-C₁₁ substituted or unsubstituted heteroaryl; or R^(21a) and R^(21b) can be taken together to form a substituted or unsubstituted ring having from 3 to 10 carbon atoms and from 0 to 3 heteroatoms chosen from oxygen, nitrogen, and sulfur; xiii) —[C(R^(10a))(R^(10b))]_(y)CN; xiv) —[C(R^(10a))(R^(10b))]_(y)NO₂; xv) —[C(R^(10a))(R^(10b))]_(y)SO₂R²²; R²² is hydrogen, hydroxyl, substituted or unsubstituted C₁-C₄ linear or branched alkyl; substituted or unsubstituted C₆, C₁₀, or C₁₄ aryl; C₇-C₁₅ alkylenearyl; C₁-C₉ substituted or unsubstituted heterocyclic; or C₁-C₁₁ substituted or unsubstituted heteroaryl; and xvi) halogen; xvii) —[C(R^(10a))(R^(10b))]_(y)(CH_(j′)X_(k′))_(h)CH_(j)X_(k); wherein X is halogen, the index j is an integer from 0 to 2, the index k is an integer from 1 to 3, j+k=3; the index j′ is an integer from 0 to 2, the index k′ is and integer from 0 to 2, j′+k′=2; the index h is from 0 to 5; R^(10a) and R^(10b) are each independently hydrogen or C₁-C₄ alkyl; and the index y is from 0 to 5; R¹ and R⁸ can be taken together to from a 5 to 7 member ring containing from 3 to 7 carbon atoms and from 0 to 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms can be substituted, unsubstituted, or a carbonyl unit.
 17. A article according to claim 16, wherein the substitutions are each independently chosen from: i) C₁-C₁₂ linear, branched, or cyclic alkyl, alkenyl, and alkynyl; ii) C₁-C₁₂ linear, branched, or cyclic alkoxy, alkenyloxy, and alkynyloxy; iii) C₁-C₁₂ linear, branched, or cyclic haloalkyl, haloalkenyl, and haloalkynyl; iv) C₆ or C₁₀ aryl; v) C₆ or C₁₀ alkylenearyl; vi) C₁-C₉ heterocyclic rings; vii) C₁-C₉ heteroaryl rings; viii) —(CR^(102a)R^(102b))_(z)OR¹⁰¹; ix) —(CR^(102a)R^(102b))_(z)C(O)R¹⁰¹; x) —(CR^(102a)R^(102b))_(z)C(O)OR¹⁰¹; xi) —(CR^(102a)R^(102b))_(z)C(O)N(R¹⁰¹)₂; xii) —(CR^(102a)R^(102b))_(z)N(R101)₂; xiii) halogen; xiv) —(CR^(102a)R^(102b))_(z)CN; xv) —(CR^(102a)R^(102b))_(z)NO₂; xvi) —CH_(j)X_(k); wherein X is halogen, the index j is an integer from 0 to 2, j+k=3; for example, xvii) —(CR^(102a)R^(102b))_(z)SR¹⁰¹; xviii) —(CR^(102a)R^(102b))^(z)SO₂R¹⁰¹ and xix) —(CR^(102a)R^(102b))_(z)SO₃R¹⁰¹; wherein each R¹⁰¹ is independently hydrogen, substituted or unsubstituted C₁-C₆ linear, branched, or cyclic alkyl, phenyl, benzyl, heterocyclic, or heteroaryl; or two R¹⁰¹ units can be taken together to form a ring comprising 3-7 atoms; R^(102a) and R^(102b) are each independently hydrogen or C₁-C₄ linear or branched alkyl; the index z is from 0 to
 4. 18. The article according to claim 16, wherein R² to R⁷ are each hydrogen.
 19. The article according to claim 16, wherein R¹ and R⁸ can be taken together to from 6 member ring containing from 4 to 5 carbon atoms and 1 or 2 heteroatoms chosen from oxygen, sulfur, or nitrogen, wherein one or more of the carbon atoms is a carbonyl unit.
 20. The article according to claim 16, wherein the compound is chosen from: i) benzo[d]isochromen-1(3H)-one having the formula:

ii) 1H-henzo[d]isoquinoline-1,3(2H)-dione having the formula:

and iii) 2,3-dihydro-1H-benzo[de]isoquinolin-1-one having the formula:


21. The article according to claim 16, wherein the compound is benzo[de]-isochromene-1,3-dione having the formula:


22. The article according to claim 16, wherein the compound has the formula:

R¹ and R⁸ are each independently: i) hydrogen; or ii) —C(O)R¹⁴; wherein R¹⁴ is —OR¹⁵ or —N(R^(16a))(R^(16b)); R¹⁵ is hydrogen or methyl; R^(16a) and R^(16b) are each independently hydrogen or methyl.
 23. The article according to claim 16, wherein the compound is naphthalene-1,8-dicarobxamide having the formula:


24. The article according to claim 16, wherein the oxygen scavenger is an N-allylic amide or N-benzylic amide.
 25. The article according to claim 16, wherein the base polymer comprises a polyester.
 26. (canceled) 